Quote Originally Posted by T 20 View Post
Hi Ed.

This raises a few questions, if these old girls were hot blued wouldn't the soft solder melt out ?

Or is it possible that they would have been soldered together after bluing ?

Or could it be that they were originally fume/rust blued ?


I only ask as I've read somewhere that older 12 bore side by sides are not recommended to be hot blued as the barrels can part company with each other as the solder melts.



All the best Mick
Hi Mate, just re-visited this and see Baz has the gen for you

ATB, Ed